Standard: | GB, DIN, ASTM, AISI |
---|---|
Application: | Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard |
Material: | Silicon Carbide |
Type: | Wear Resistant Pipe |
Product Name: | Rbsic Silicon Carbide Ceramic Linings Lined Pipe |
MOQ: | 1pieces |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Reaction bonded silicon carbide is a multi-phased material typically containing 7-15% silicon metal, some minor amount of
unreacted carbon, with the remaining body being SiC. Reaction bonded SiC materials are manufactured utilizing a variety of
processes depending on desired final product geometry, configuration, and required tolerances.
Reaction bonded silicon carbide has proven to be an excellent material choice for wear applications such as pipe liners, flow
control chokes and larger wear components in the mining as well as other industries. CALSIC RB offers an economical and reliable
material option for many applications where the corrosion resistance or wear resistance of CALSIC S (sintered silicon carbide) is
not necessary.
Typical properties of silicon carbide are:
Excellent thermal shock resistance
Excellent hot strength
Excellent abrasion resistance
Good thermal conductivity
Relatively low coefficient of thermal expansion
Typical applications for silicon carbide are:
Kiln furniture for powder metal and ceramic processing
Kiln components including:
hearths
entrance tiles
skid rails
Series of wear resistant panel
· Rubber alumina ceramic panel
· Ceramic pulley lagging
· Two-In-one wear resistant/composite panel with CN layer
· ZTA wear resistant panel
· Polyurethane wear resistant panel
· Silicon carbide wear resistant panel
Name |
Project |
Unit |
Index |
Rubber |
Fracture Toughness |
20"C,Mpa % |
3.65 |
Thermal Shock Resistance |
ATc,°C |
250 |
|
Surface Roughness |
um |
V.9 |
|
Water Absorption |
50.01 |
>1.2 |
|
Density |
g/cm3 |
||
Elongation |
% |
500 |
|
Tensile Strength |
Mpa |
19.6 |
|
Shore Hardness |
HA |
60±5 |
|
Peel Strength |
Mpa |
212 |
|
Temperature Range |
•C |
-40-120 |
|
Polyurethane |
Elongation |
% |
350 |
Tensile Strength |
Mpa |
25 |
|
Shore Hardness |
HA |
85±5 |
|
Steel |
Carbon Steel Plate |
Gpa |
Q235B.A36 |
Thickness |
3-10 |
||
Bolt |
High Strength Bolts |
4.8Z8.8 |
|
Abrasion Resistance |
P=74N. n=800rpm. t=30min |
0.0005g |
Color | Black |
Density | 3.02/cm3 |
Apparent Porocity | <0.1% |
Hardness |
2400Kg/mm2 |
Temperature | ≤1380ºC |
Bending Strength |
250MPa (20ºC) |
Modulus of Elasticity | 330GPa (20ºC) 300GPa (1200ºC) |
Coefficient of Thermal Conductivity | 45W/m.k (1200ºC) |
Coefficient of Thermal Expansion | 4.5K (-3)*10 (-5) |
Mohs Hardness | 13 |
ZIBO CHENYI offers wear and anti-impact ceramics, in combination with our experienced and competent staff, ensure the increased efficiency and service life of all equipment and materials to which they are applied.
Established Ultrafine Energy Efficiency Technology Research Institute
Increase the lifespan of wearable parts
New improved technology and products
Minimal downtime to reduce the delay in production
Variety of wear combating options available as a stop solution
Strong fouc on product innovation supported by Chinese Academy of Sciences
Customizable application techniques to suit any wear problem
Q: Are you a trading company or manufacturer?
A: We are a factory, real manufacturer. 50,000Sqm, 300 workers.
Q: Is the sample free?
A: Yes, we offer free samples at weight 1KG.
The sample air shipping fee will be refunded for the first PO.
Q: How long is your delivery time?
A: For stock product: prompt delivery.
For No none-stock product: 15-35days against PO and Desposit.
Q: What are your terms of payment?
A: 30% T/T in advance, balance against B/L copy after shipment.
Q: Accept customized?
A: Can be customized as per request.
Any inquiry pls feel free to contact us for more communication.
Suppliers with verified business licenses